Q1: Kouman mwen ta dwe chwazi soude consommables lè soude S275NH tiyo asye?
Li rekòmande pou itilize elektwòd idwojèn ki ba {0} Pou soudi ak soude ARC (SAW), konbinezon an flux F7A2-EM12K se apwopriye. Fòs nan consommables yo soude yo ta dwe yon ti kras pi wo pase sa yo ki an metal la baz (egzanp, fòs rupture pi wo a 480 MPa), men pa twò wo pou fè pou evite soude embrittlement. Lè w ap achte, konfime ke consommables yo soude konfòme yo avèk AWS A5.1 oswa EN ISO 2560 estanda. Pou aplikasyon pou ba -tanperati, yo dwe verifye enèji enpak degre -20 nan soude consommables yo.
Q2: Ki sa ki paramèt yo ta dwe konsidere lè frèt - Bending S275NH tiyo asye?
The cold-bending radius is generally no less than three times the outer diameter of the steel pipe to prevent cracking of the outer wall. Before processing, ensure that the steel pipe is in a normalized state to avoid uneven springback due to residual stress. For thick-walled pipe (e.g., t>12 mm), prechofe nan 80-120 degre rekòmande diminye redi travay frèt. Apre koube, enspekte sifas la pou ondilasyon oswa microcracks, ak fè tès patikil mayetik (MT) si sa nesesè. Lè yo trete fòm konplèks, yo ka itilize yon pwosesis pwogresis pwogresis pwogresis pou diminye souch lokal yo.
Q3: Ki sa ki kondisyon yo ki espesyal pou koupe tèmik nan tiyo asye S275NH?
Pandan koupe flanm dife, pite a oksijèn (pi gran pase oswa egal a 99.5%) ak tanperati chofe (apeprè 200 degre) dwe kontwole yo anpeche redi nan kwen an koupe. Plasma koupe se pi apwopriye pou mens - tiyo gwo ranpa (t<10 mm), as it minimizes the heat-affected zone. Laser cutting offers high precision, but power and speed must be optimized to prevent slag adhesion. After cutting, grinding is required to remove scale and burrs, especially around weld grooves. For critical components, hardness testing is recommended to confirm that cutting has not caused local embrittlement.
Q4: Kouman mwen ka evite deformation apre soude S275NH tiyo asye?
Sèvi ak yon sekans simetrik soude (tankou sote soude oswa segman tounen - koupe) nan balans distribisyon chalè. Pou soud long, sèvi ak yon kranpon oswa sipò tanporè an sekirite tiyo a. Kenbe tanperati a interpass anba a 250 degre pou fè pou evite surchof ki ka mennen nan coarsening nan grenn yo. Ti - tiyo ki gen gwo ranpa (t <6 mm) ta dwe soude ak vitès ki ba aktyèl ak gwo diminye opinyon chalè. Post - Deformation Weld ka korije nan koreksyon mekanik (tankou redresman idwolik) oswa chofaj lokalize, men fè atansyon pou fè pou evite twòp travay frèt.
Q5: Ki sa ki se kèk teknik pou D '(vire, perçage) S275NH tiyo asye?
Sèvi ak zouti koupe carbure (tankou ISO K10 - K20) epi kenbe bor koupe byen file diminye risk pou yo redi travay. Vitès koupe nan 80 - 120 m/min ak manje nan 0.1 - 0.3 mm/r yo rekòmande. Sèvi ak awozaj lè perçage pou fè pou evite devyasyon dyamèt twou ki te koze pa bati-up kwen. Pou koneksyon wo-fòs fil, li rekòmande yo pre-fè egzèsis twou a 5% -10% pi gwo pase dyamèt la estanda anvan frapan. Apre D ', anrejistreman yo dwe netwaye pou anpeche etensèl estatik pou limen lwil ak kontaminan.