Kesyon 1: Ki kondisyon definisyon pou tuyaux rezistan a H₂s korozyon nan API 5L spesifikasyon?
When the partial pressure of H₂S reaches 300Pa, the pipe used must have the performance of acid corrosion resistance. This kind of pipeline used in acid environment is acid-resistant line pipe. Pipelines used in this environment have special requirements for the carbon content, sulfur-phosphorus content, calcium-sulfur ratio, and flaw detection of the pipe, and Mande pou HIC (idwojèn-pwovoke fann) ak SSC (SULFIDE estrès fann) tès . estanda yo aplikasyon prensipal yo API 5L ak ISO 31833.
Kesyon 2: Kouman se tès la HIC nan H₂S ki reziste tiyo liy ki fèt anba API 5L spesifikasyon?
The implementation standard of HIC test is NACE TM0284, and the sample size is 100mm long and 20mm wide. The test sample is placed in two standard test solutions: solution A (sodium chloride and acetic acid solution saturated with H₂S at room temperature and pressure) and solution B (synthetic seawater solution saturated with H₂S at room temperature and pressure), and the test time is 96 Orè . Gen twa endikatè pou evalyasyon: rapò sansiblite krak CSR mwens pase oswa egal a 2%, rapò longè krak CLR mwens pase oswa egal a 15%, ak rapò epesè krak CTR mwens pase oswa egal a 5%.
Kesyon 3: Ki sa ki metòd yo pou tès SSC nan tiyo liy H₂S ki reziste anba API 5L spesifikasyon?
Se tès la SSC aplike an akò ak NACE TM0177, ak gwosè a echantiyon nan kat-pwen metòd la koube se 115mm × 15mm × 5mm . Gen 4 metòd tès:
Tès Metòd A - NACE estanda tès rupture: maksimòm ki pa echèk estrès nan 720 èdtan
Tès Metòd B - NACE Creole Bend Tès: Maksimòm estrès ki pa echèk nan 720 èdtan
Tès Metòd C-NACE Creole C-Ring Tès: Maksimòm estrès ki pa echèk nan 720 èdtan
Tès Metòd D - NACE Creole Double Cantilever Beam (DCB) Tès: Mwayèn KISSC (SSC Limit Estrès Entansite koyefisyan) nan echantiyon tès repete pou tès valab . Genyen tou 3 solisyon tès, solisyon A se yon asid, tampon yon sèl {{3}
Kesyon 4: Ki klas oswa kalite tuyaux nan API 5L estanda yo pi apwopriye pou rezistans anviwònman H₂s?
Pipeline tiyo nan PSL -2 klas anba API 5L estanda se relativman pi apwopriye pou H₂s rezistans anviwònman . Anplis kondisyon ki nan PSL -1, PSL {{4} NACE standard involves the performance of steel pipes in environments containing corrosive media (such as H₂S and CO₂), API 5L GR. B PSL-1 NACE steel pipes are designed and manufactured with the potential effects of these corrosive media in mind, have better corrosion resistance, and are suitable for harsh oil and gas environments, where they have a certain resistance to corrosion such as H₂s .
Kesyon 5: Ki mezi yo te pran nan API 5L spesifikasyon an asire rezistans yo H₂s nan tiyo liy?
Kontwòl konpozisyon chimik: Limite kontni eleman ki nan tiyo asye ki ka afekte rezistans korozyon, tankou souf, fosfò, elatriye ., pou asire ke konpozisyon chimik tiyo asye a satisfè egzijans rezistans espesifik . pou egzanp, yo ka amelyore oswa yon moun ki gen mwens ladan yo pou yo ka amelyore pwòp yo ak yon moun ki gen mwens ke yo ka amelyore yo, epi yo ka amelyore yo pou yo amelyore netwaye yo epi yo ka amelyore pwòp yo, epi yo ka amelyore pwòp yo, epi yo ka amelyore pwòp yo, epi yo ka amelyore pwòp yo, yo ka amelyore yo, yo ka amelyore yo, yo ka amelyore yo. 0 . 09%, s mwens pase oswa egal a 0.005%, p mwens pase oswa egal a 0.01%, o mwens pase oswa egal a 0.002%, ak adopte microalloying, elatriye.
Tès ak sètifikasyon: tiyo asye dwe pase yon seri de tès, ki gen ladan men pa limite a tès korozyon, idwojèn SULFIDE estrès korozyon fann (HIC) tès yo, estrès-oryante idwojèn-induit fann (SOHIC) tès yo, ak tès fatig korozyon, asire pèfòmans yo nan anviwònman h₂s {{{{{{
Faktori Pwosesis Kontwòl: Kontwole pwosesis la fabrikasyon nan tiyo asye, ki gen ladan tretman chalè, soude ak tretman sifas yo, asire rezistans a korozyon nan tiyo asye