API 5CT Casing Tiyo
Klas: H40, J55, K55, L80, L80-13Cr, L80-9Cr, N80-1, N80Q, P110
O.D: 4 1/2"-20"
Longè: R1, R2, R3
Koneksyon: STC, LTC, BTC, Koneksyon Premium (VAM TOP, NEW VAM, PH-6)
Tablo done tiyo aman
| Etikèta | OD mm |
Nominal Lineyè Massb,c T&C kg/m |
WT t mm |
Kalite fen-finid | ||||||||
| H40 | J55 K55 |
M65 | L80 R95 |
N80 Kalite 1, Q |
C90 T95 |
P110 | Q125 | |||||
| 1 | 2 | |||||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 |
| 4-1/2 4-1/2 4-1/2 4-1/2 4-1/2 |
9.50 10.50 11.60 13.50 15.10 |
114.30 114.30 114.30 114.30 114.30 |
14.14 15.63 17.26 20.09 22.47 |
5.21 5.69 6.35 7.37 8.56 |
PS - - - - |
PS PSB PSLB - - |
PS PSB PLB PLB - |
- - PLB PLB - |
- - PLB PLB - |
- - PLB PLB - |
- - PLB PLB PLB |
- - - - PLB |
| 5 5 5 5 5 5 5 |
11.50 13.00 15.00 18.00 21.40 23.20 24.10 |
127.00 127.00 127.00 127.00 127.00 127.00 127.00 |
17.11 19.35 22.32 26.79 31.85 34.53 35.86 |
5.59 6.43 7.52 9.19 11.10 12.14 12.70 |
- - - - - - - |
PS PSLB PSLBE - - - - |
PS PSLB PLB PLB PLB - - |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - - PLB PLB PLB PLB |
| 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 5-1/2 |
14.00 15.50 17.00 20.00 23.00 26.80 29.70 32.60 35.30 38.00 40.50 43.10 |
139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 139.70 |
20.83 23.07 25.30 29.76 34.23 39.88 44.20 48.51 52.53 56.55 60.27 61.14 |
6.20 6.98 7.72 9.17 10.54 12.70 14.27 15.88 17.45 19.05 20.62 22.22 |
PS - - - - - - - - - - - |
PS PSLBE PSLBE - - - - - - - - - |
PS PSLB PLB PLB PLB - - - - - - - |
- - PLBE PLBE PLBE - - - - - - - |
- - PLBE PLBE PLBE - - - - - - - |
- - PLBE PLBE PLBE P P P P P P P |
- - PLBE PLBE PLBE - - - - - - - |
- - - - PLBE - - - - - - - |
| 6-5/8 6-5/8 6-5/8 6-5/8 |
20.00 24.00 28.00 32.00 |
168.28 168.28 168.28 168.28 |
29.76 35.72 41.67 47.62 |
7.32 8.94 10.59 12.06 |
PS - - - |
PSLB PSLBE - - |
PSLB PLB PLB - |
- PLBE PLBE PLBE |
- PLBE PLBE PLBE |
- PLBE PLBE PLBE |
- PLBE PLBE PLBE |
- - - PLBE |
| 7 7 7 7 7 7 7 |
17.00 20.00 23.00 26.00 29.00 32.00 35.00 |
177.80 177.80 177.80 177.80 177.80 177.80 177.80 |
25.30 29.76 34.23 38.69 43.16 47.62 52.09 |
5.87 6.91 8.05 9.19 10.36 11.51 12.65 |
PS PS - - - - - |
- PS PSLBE PSLBE - - - |
- PS PLB PLB PLB PLB - |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - PLB PLB PLB PLB PLB |
- - - PLB PLB PLB PLBE |
- - - - - - PLB |
| 7 7 7 7 7 7 |
38.00 42.70 46.40 50.10 53.60 57.10 |
177.80 177.80 177.80 177.80 177.80 177.80 |
56.55 63.54 69.05 74.56 79.77 84.97 |
13.72 15.88 17.45 19.05 20.62 22.22 |
- - - - - - |
- - - - - - |
- - - - - - |
PLB - - - - - |
PLB - - - - - |
PLB P P P P P |
PLB - - - - - |
PLB - - - - - |
| 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 7-5/8 |
24.00 26.40 29.70 33.70 39.00 42.80 45.30 47.10 51.20 55.30 |
193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 193.68 |
35.72 39.29 44.20 50.15 58.04 63.69 67.41 70.09 76.19 82.30 |
7.62 8.33 9.52 10.92 12.70 14.27 15.11 15.88 17.45 19.05 |
PS - - - - - - - - - |
- PSLB - - - - - - - - |
- PSLB PLB PLB - - - - - - |
- PLB PLB PLB PLB PLB PLB PLB - - |
- PLB PLB PLB PLB PLB PLB PLB - - |
- PLB PLB PLB PLB PLB PLB PLB P P |
- - PLB PLB PLB PLB PLB PLB - - |
- - - - PLB PLB PLB PLB - - |
| 7-3/4 | 46.10 | 196.85 | 68.60 | 15.11 | - | - | - | P | P | P | P | P |
| 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 8-5/8 |
24.00 28.00 32.00 36.00 40.00 44.00 49.00 |
219.08 219.08 219.08 219.08 219.08 219.08 219.08 |
35.72 41.67 47.62 53.57 59.53 65.48 72.92 |
6.71 7.72 8.94 10.16 11.43 12.70 14.15 |
- |
PS PS - PSLB PSLB PLB - |
PS PS PSLB PSLB PLB - - |
- - - PLB PLB PLB PLB |
- - - PLB PLB PLB PLBE |
- - - PLBE PLBE PLBE PLBE |
- - - PLB PLB PLB |
- - - - - PLB |
| 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 9-5/8 |
32.30 36.00 40.00 43.50 47.00 53.50 58.40 59.40 64.90 70.30 75.60 |
244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 244.48 |
48.07 53.57 59.53 64.73 69.94 79.62 86.91 88.40 96.58 104.62 112.50 |
7.92 8.94 10.03 11.05 11.99 13.84 15.11 15.47 17.07 18.64 20.24 |
PS PS - - - - - - - - - |
- PSLB PSLB - - - - - |
- PSLB PSLB PLB PLB - - - - - |
- - PLB PLB PLB PLB PLB - - - - |
- - PLB PLB PLB PLB PLB - - - |
- - PLB PLB PLB PLB PLB P P P P |
- - - PLB PLB PLB PLB - - - - |
- - - - PLB PLB PLB - - - - |
| 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 10-3/4 |
32.75 40.50 45.50 51.00 55.50 60.70 65.70 73.20 79.20 85.30 |
273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 273.05 |
48.74 60.27 67.71 75.90 82.59 90.33 97.77 108.93 117.86 126.94 |
7.09 8.89 10.16 11.43 12.57 13.84 15.11 17.07 18.64 20.24 |
PS PS - - - - - - - - |
- PSB PSB PSB - - - - - - |
- PSB PSB PSB PSB - - - - - |
- - - PSB PSB - - - - - |
- - - PSB PSB - - - - - |
- - - PSB PSB PSB PSB P P P |
- - - PSB PSB PSB PSB - - - |
- - - - - PSB PSB - - - |
| 11-3/4 11-3/4 11-3/4 11-3/4 11-3/4 11-3/4 |
42.00 47.00 54.00 60.00 65.00 71.00 |
298.45 298.45 298.45 298.45 298.45 298.45 |
62.50 69.94 80.36 89.29 96.73 105.66 |
8.46 9.53 11.05 12.42 13.56 14.78 |
PS - - - - - |
- PSB PSB PSB - - |
- PSB PSB PSB - - |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
- - - PSB P P |
| 13-3/8 13-3/8 13-3/8 13-3/8 13-3/8 |
48.00 54.50 61.00 68.00 72.00 |
339.72 339.72 339.72 339.72 339.72 |
71.43 81.10 90.78 101.19 107.15 |
8.38 9.65 10.92 12.19 13.06 |
PS - - - - |
- PSB PSB PSB - |
- PSB PSB PSB - |
- - - PSB PSB |
- - - PSB PSB |
- - - PSB PSB |
- - - PSB PSB |
- - - - PSB |
| 16 16 16 16 |
65.00 75.00 84.00 109.00 |
406.40 406.40 406.40 406.40 |
96.73 111.61 125.01 162.21 |
9.53 11.13 12.57 16.66 |
PS - - - |
- PSB PSB P |
- PSB PSB - |
- - - P |
- - - P |
- - - - |
- - - P |
- - - P |
| 18-5/8 | 87.50 | 473.08 | 130.21 | 11.05 | PS | PSB | PSB | - | - | - | - | - |
| 20 20 20 |
94.00 106.50 133.00 |
508.00 508.00 508.00 |
139.89 158.49 197.93 |
11.13 12.70 16.13 |
PSL - - |
PSLB PSLB PSLB |
PSLB PSLB - |
- - - |
- - - |
- - - |
- - - |
- - - |
| P=Plan fen; S=kout fil wonn; L=Long fil wonn; B - Fil pou kontre; | ||||||||||||
|
a: Etikèt yo se pou enfòmasyon ak asistans nan kòmande. b: Mas nominal lineyè (col{0}}) yo montre pou enfòmasyon sèlman. c: Dansite martensitic kwòm asye (L80 Kalite 9Cr ak 13Cr) yo diferan de asye kabòn. Se poutèt sa, mas yo montre yo pa egzat pou asye kwòm martensitic. Yo ka itilize yon faktè koreksyon mas 0.989. d: Boîtier contrefort ki disponib ak regualr, couplages clearance espesyal ou couplages clearance espesyal ak biseau espesyal. |
||||||||||||
API 5CT MATERYÈL KONPOZISYON CHIMIK
| Gwoup | Klas | Kalite | C | Mn | Mo | Kr |
Ni max |
Cu max |
P max |
S max |
Si max |
||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| min | max | min | max | min | max | min | max | ||||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | 13 | 14 | 15 | 16 |
|
1 |
H40 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
J55 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
K55 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
N80 |
1 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
N80 |
Q |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
|
R95 |
– |
– |
0.45 c |
– |
1.9 |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
0.45 |
|
|
2 |
M65 |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.03 |
0.03 |
– |
|
L80 |
1 |
– |
0.43 a |
– |
1.9 |
– |
– |
– |
– |
0.25 |
0.35 |
0.03 |
0.03 |
0.45 |
|
|
L80 |
9Kr |
– |
0.15 |
0.3 |
0.6 |
0.9 |
1.1 |
8 |
10 |
0.5 |
0.25 |
0.02 |
0.01 |
1 |
|
|
L80 |
13Kr |
0.15 |
0.22 |
0.25 |
1 |
– |
– |
12 |
14 |
0.5 |
0.25 |
0.02 |
0.01 |
1 |
|
|
C90 |
1 |
– |
0.35 |
– |
1.2 |
0.25 b |
0.85 |
– |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
|
T95 |
1 |
– |
0.35 |
– |
1.2 |
0.25 d |
0.85 |
0.4 |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
|
C110 |
– |
– |
0.35 |
– |
1.2 |
0.25 |
1 |
0.4 |
1.5 |
0.99 |
– |
0.02 |
0.005 |
– |
|
|
3 |
P110 |
e |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.030 e |
0.030 e |
– |
|
4 |
Q125 |
1 |
– |
0.35 |
1.35 |
– |
0.85 |
– |
1.5 |
0.99 |
– |
0.02 |
0.01 |
– |
|
| a Kontni kabòn pou L80 ka ogmante jiska 0.50% maksimòm si pwodwi a lwil oliv -toufè. b Kontni molybdène pou Klas C90 Kalite 1 pa gen okenn tolerans minimòm si epesè miray la se mwens pase 17.78 mm. c Kontni kabòn pou R95 ka ogmante jiska 0.55% maksimòm si pwodwi a lwil oliv -toufè. d Kontni molybdène pou T95 Kalite 1 ka diminye a 0.15% minimòm si epesè miray la se mwens pase 17.78 mm. e Pou klas EW P110, kontni fosfò a dwe 0.020% maksimòm ak kontni souf la dwe 0.010% maksimòm. NL=pa gen limit. Eleman yo montre yo dwe rapòte nan analiz pwodwi. |
|||||||||||||||
MATERIAL TIYO CASING - PWOPRIYETE MEKANIK
| Gwoup |
Klas |
Kalite |
Total elongasyon anba chaj % |
Sede fòs MPa |
Tensile fòs min. MPa |
Dite a max. |
Espesifye miray epesè mm |
Akseptab dite varyasyon b HRC |
||
|---|---|---|---|---|---|---|---|---|---|---|
| min | max | HRC | HBW | |||||||
| 1 | 2 | 3 | 4 | 5 | 6 | 7 | 8 | 9 | 10 | 11 |
| 1 |
H40 |
– |
0.5 |
276 |
552 |
414 |
– |
– |
– |
– |
|
J55 |
– |
0.5 |
379 |
552 |
517 |
– |
– |
– |
– |
|
|
K55 |
– |
0.5 |
379 |
552 |
655 |
– |
– |
– |
– |
|
|
N80 |
1 |
0.5 |
552 |
758 |
689 |
– |
– |
– |
– |
|
|
N80 |
Q |
0.5 |
552 |
758 |
689 |
– |
– |
– |
– |
|
|
R95 |
– |
0.5 |
655 |
758 |
724 |
– |
– |
– |
– |
|
| 2 |
M65 |
– |
0.5 |
448 |
586 |
586 |
22 |
235 |
– |
– |
|
L80 |
1 |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
L80 |
9Kr |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
L80 |
13Kr |
0.5 |
552 |
655 |
655 |
23 |
241 |
– |
– |
|
|
C90 |
1 |
0.5 |
621 |
724 |
689 |
25.4 |
255 |
Mwens pase oswa egal a 12.70 12.71 to 19.04 19.05 to 25.39 Pi gran pase oswa egal a 25.40 |
3.0 4.0 5.0 6.0 |
|
|
T95 |
1 |
0.5 |
655 |
758 |
724 |
25.4 |
255 |
Mwens pase oswa egal a 12.70 12.71 to 19.04 19.05 to 25.39 Pi gran pase oswa egal a 25.40 |
3.0 4.0 5.0 6.0 |
|
|
C110 |
– |
0.7 |
758 |
828 |
793 |
30 |
286 |
Mwens pase oswa egal a 12.70 12.71 pou 19.0 19.05 pou 25.39 Pi gran pase oswa egal a 25.40 |
3.0 4.0 5.0 6.0 |
|
| 3 |
P110 |
– |
0.6 |
758 |
965 |
862 |
– |
– |
– |
– |
| 4 |
Q125 |
1 |
0.65 |
862 |
1034 |
931 |
b |
– |
Mwens pase oswa egal a 12.70 12.71 a 19.04 Pi gran pase oswa egal a 19.05 |
3.0 4.0 5.0 |
| a Nan ka diskisyon, yo dwe itilize tès dite laboratwa Rockwell C kòm metòd abit. b Pa gen limit dite yo espesifye, men varyasyon maksimòm nan limite kòm yon kontwòl fabrikasyon an akò ak 7.8 ak 7.9 nan API Spec. 5CT. |
||||||||||
Hot Tags: api 5ct H40, J55, K55, L80, L80 - 13Cr, L80-9Cr, N80-1, N80Q, P110 bwat tiyo, Lachin, manifaktirè, founisè, faktori, konpayi, ekspòtatè, vandè, mak, enpòte, achte, pi bon, kalite siperyè